The Effect of Multi-walled Carbon Nanotubes, as the Reinforcement Phase, on the Hardness and Bending Strength of Aluminum Alloy 7075 | ||
| Journal of Stress Analysis | ||
| دوره 6، شماره 1، آذر 2021، صفحه 61-66 اصل مقاله (3.63 M) | ||
| نوع مقاله: Original Research Paper | ||
| شناسه دیجیتال (DOI): 10.22084/jrstan.2021.21335.1140 | ||
| نویسندگان | ||
| F. Barati* ؛ M. Esfandiari | ||
| Department of Mechanical Engineering, Hamedan Branch, Islamic Azad University, Hamedan, Iran. | ||
| چکیده | ||
| In the present investigation, to fabricate Nano-composites made of wrought aluminum alloy 7075 and multi-walled carbon nanotubes, carbon nanotubes and the alloy powders were initially dispersed in ethanol using an ultrasonic shaker to form a primary mixture. The milled powder mixture was converted into the final specimens by Spark-Plasma Sintering. To achieve a uniform distribution of carbon nanotubes in the matrix alloy, ethanol or stearic acid can be used as a Processing Control Agent (PCA). For each of the seven specimens, a series of tests were performed to study the effects of the reinforcement phase on the base alloy. As shown, the reinforced specimens were harder compared to the pure Al7075 and the sample reinforced with 1wt% of multi-walled carbon nanotubes has both the highest hardness and flexural strength among all the specimens. Additionally, when the weight fraction reached 2%, there was a noticeable drop in the mechanical properties. This novel alloy produced by powder metalurgy can be very helpul for industrial application where the increase in strength and hardness is deireable. | ||
| کلیدواژهها | ||
| High-energy ball mill؛ Multi-walled carbon nanotubes؛ Nanocomposites؛ Spark-plasma sintering | ||
| مراجع | ||
|
[1] H.T. Son, T.S. Kim, C. Suryanarayana, B.S. Chun, Homogeneous dispersion of graphite in a 6061 aluminum alloy by ball milling, Mater. Sci. Eng. A, 348(1-2) (2003) 163-169. [2] Y. Kawamura, H. Mano, A. Inoue, Nanocrystalline aluminum bulk alloys with a high strength of 1420MPa produced by the consolidation of amorphous powders, Scr. Mater., 44 (8-9) (2001) 1599-1604. [3] H. Lianxi, L. Zuyan, W. Erde, Microstructure and mechanical properties of 2024 aluminum alloy consolidated from rapidly solidified alloy powders, Mater. Sci. Eng. A, 323 (1-2) (2002) 213-217. [4] H. So, W.C. Li, H.K. Hsieh, Assessment of the powder extrusion of silicon- aluminium alloy, J. Mater. Process. Technol., 114(1) (2001) 18-21. [5] D.W. Heard, I.W. Donaldson, D.P. Bishop, Metallurgical assessment of a hypereutectic aluminum–silicon P/M alloy, J. Mater. Process. Technol., 209(18-19) (2009) 5902-5911. [6] T. Hasegaw, T. Yasuno, T. Nagai, T. Takahashi, Origin of superplastic elongation in aluminum alloys produced by mechanical milling, Acta Mater., 46(17) (1998) 6001-6007. [7] R.S. Ruof, D.C. Lorents, Mechanical and thermalproperties of carbon nanotubes, Carbon, 33(7) (1995) 925-930. [8] S. Iijima, Helical Microtubules of graphitic carbon, Nature, 354 (1991) 56-58. [9] S. Iijima, T. Ichihasi, Single-shell carbon nanotubes of 1-nm diameter, Nature, 363 (1993) 603-605. [10] V.N. Popov, Carbon nanotubes: Properties and applications, Mater. Sci. Eng. R, 43 (2004) 61-102. [11] M.F. Yu, B.S. Files, S. Arepalli, R.S. Ruoff, Tensile loading of ropes of single wall carbon nanotubes and their mechanical properties, Phys. Rev. Lett., 84(24) (2000) 5552-5555. [12] G. Overney, W. Zhong, D. Dománek, Structural rigidity and low frequency vibrational modes of long carbon tubules, Z. Phys. D Atom. MOL. CL., 27 (1993) 93-96. [13] S.I. Cha, K.T. Kim, S.N. Arshad, C.B. Mo, S.H. Hong, Extraordinary strengthening effect of carbon nanotubes in metal-matrix nano-composites processed by molecular-level mixing, Adv. Mater., 17(11) (2005) 1377-1381. [14] R. George, K.T. Kashyap, R. Rahul, S. Yamdagni, Strengthening in aluminium/CNT composites, Scr. Mater., 53(10) (2005) 1159-1163. [15] C. Deng, X.X. Zhang, D. Wang, Q. Lin, A. Li, Preparation and characterization of carbon nanotubes / aluminium matrix composites, Mater. Lett., 61(8-9) (2007) 1725-1728. [16] C.F. Deng, X.X. Zhang, D.Z. Wang, Y.X. Ma, Calorimetric study of carbon nanotubes and aluminum, Mater. Lett., 61(14-15) (2007) 3221-3223. [17] C.F. Deng, Y.X. Ma, P. Zhang, X.X. Zhang, D.Z. Wang, Thermal expansion behaviors of aluminium composites reinforced with carbon nanotubes, Mater. Lett., 62(15) (2008) 2301-2303. [18] U. Anselmi-Tamburini, J.E. Garay, Z.A. Munir, A. Tacca, F. Maglia, G. Spinolo, Spark plasma sintering and characterization of bulk nanostructured fully stabilized zirconia: Part I, densification studies, J. Mater. Res., 19(11) (2004) 3255-3262. [19] A. Khalil, Synthesis and Wear Behaviour of Aluminium 6061 Alloy Reinforced with CNT. Master Thesis, King Fahd University of Petroleum and Minerals, Dhahran, Saudi Arabia, (2012). [20] A.H. Javadi, Sh. Mirdamadi, M.A. Faghihisani, S. Shakhesi, R. Soltani, Fabrication of well-dispersed, multiwalled carbon nanotubes reinforced aluminum matrix composites, New Carbon Mater., 27(3) (2012) 161-165. [21] L. Wang, H. Choi, J.M. Myoung, W. Lee, Mechanical alloying of multi- walled carbon nanotubes and aluminum powders for the preparation of carbon/metal composites, Carbon, 47(15) (2009) 3427-3433. [22] ASTM C1161, Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature, (1996). [23] ASTM E92, Standard Test Method for Vickers Hardness of Metallic Materials, (1997). [24] F. Barati, M. Latifi, E. Moayerifar, M.H. Mosallanejad, A. Saboori, Novel AM60-SiO2 nanocomposite produced via ultrasound-assisted casting; production and characterization, Materials, 12(23) (2019) 3976. [25] F. Fereshteh-Saniee, F. Barati, H. Badnava, Kh. Fallah Nejad, An exponential material model for prediction of the flow curves of several AZ series magnesium alloys in tension and compression, Mater. Des., 35 (2012) 1-11. [26] Z. Hosseini Tabar, F. Barati, Effect of SiC particles on fatigue life of al-matrix composites, J. Stress Anal., 4(1) (2019) 73-88. [27] M.M. Amiri, F. Fereshteh-Saniee, An Experimental investigation on the effect of cooling rate during combined continuous casting and rolling process on mechanical properties of 7075 aluminum alloy, Trans. Indian Inst. Met., 73 (2020) 441-448. [28] D. Zhou, T. Li, S. Xu, J. Liu, Microstructure and mechanical properties of adding adhesive-layer laser-welded joints of DP590 dual-phas steel and 6061 aluminum alloy, Trans. Indian Inst. Met., 72 (2019) 3295-3304. [29] H. Li, M. Ramezani, Z. Chen, S. Singamneni, Effects of process parameters on temperature and stress distributions during selective laser melting of Ti-6Al-4V, Trans. Indian Inst. Met.,72 (2019) 3201-3214. [30] M. Arefi, E. Mohammad-Rezaei Bidgoli, R. Dimitri, F. Tornaben, Free vibrations of functionally graded polymer composite nanoplates reinforced with graphene nanoplatelets, Aerosp. Sci. Technol., 81 (2019) 108-117. [31] M. Arefi, E. Mohammad-Rezaei Bidgoli, R. Dimitri, M. Bacciocchi, F. Tornabene, Nonlocal bending analysis of curved nanobeams reinforced by graphene nanoplatelets, Aerosp. Sci. Technol., 166 (2019) 1-12. [32] M. Arefi, E. Mohammad-Rezaei Bidgoli, R. Dimitri, F. Tornabene, J.N. Reddy, Size-dependent free vibrations of FG polymer composite curved nanobeams reinforced with graphene nanoplatelets resting on pasternak foundations, Appl. Sci., 9(8) (2019) 1580. [33] M. Mohammadi, M. Arefi, R. Dimitri, F. Tornabene, Higher-order thermo-elastic analysis of FGCNTRC cylindrical vessels surrounded by a pasternak foundation, Nanomaterials, 9(1) (2019) 79. [34] M. Arefi, S. Kiani Moghaddam, E. MohammadRezaei Bidgoli, M. Kiani, O. Civalek, Analysis of graphene nanoplatelet reinforced cylindrical shell subjected to thermo-mechanical loads, Composite Structures, 255 (2021) 112924. [35] E. Mohammad-Rezaei Bidgoli, M. Arefi, Free vibration analysis of micro plate reinforced with functionally graded graphene nanoplatelets based on modified strain-gradient formulation, J. Sandw. Struct. Mater., 23 (2) (2021) 436-472. | ||
|